Knowledge of vacuum heat treatment
Time：2015-06-17 09:02
1. Titanium vacuum furnace process, should not use nitrogen as the cooling gas, because titanium and nitrogen at high temperatures, to form titanium nitride gold.
2. Vacuum furnace part in all activities in connection rubber O-ring seals the connection, this section are cooled by water.
3. Hardening of the workpiece in a vacuum, you should use a vacuum quenching oil, this oil has a lower saturation vapor pressure.
4. Vacuum furnace maintenance should charge under vacuum or nitrogen status, avoid breathing normally when not absorb moisture.
5. Domestic vacuum furnace pressure rise rate should not exceed 1.33Pa / h, certain standards for foreign companies 0.67Pa / h
6. Vacuum heating to radiation main piece in the furnace should be kept spacing.
7. Heating process, the workpiece material and the furnace will be deflated to a vacuum degree drop.
8. The heating temperature vacuum annealing, vacuum annealing, vacuum and vacuum aging solution treatment temperature is generally the same as conventional treatment and heating.
9. Vacuum furnace should have a fast-cooling device. Cooling water pressure should be greater than 0.2Mpa, traffic should be adjustable.
Protech Experimental Furnace (http://www.lab-furnace.com) is a professional production of energy-saving high-temperature furnace and kiln manufacturers, product range include: high-temperature furnace, the current high-temperature furnace, box furnace, laboratory furnace, high temperature melting block furnace production technology and production process to achieve world-class level wholeheartedly welcome the high temperature furnace, box furnace, laboratory furnace, high temperature furnace frit interested friends come to visit, study, discuss business!
For Laboratory Muffle furnace, Tube furnace, Dental furnace, please contact us.
HOT PRODUCTS
-
-
High temperature box resistance furnace
-
Large diameter double temperature zone rotating tube furnace
-
English
简体中文
French
日本語
Korean
Português
Русский
Spanish